Product Introduction
Aconia 3D Master, the next generation of Aconia 3D Multilayer, redefines multilayer zirconia with superior performance in aesthetics, function, and stability. It is ideal for the efficient fabrication of monolithic aesthetic crowns to wide-span bridges, including implant-supported long bridges.

Features

Durability Redefined

Durability Redefined

With flexural strength of 800 - 1200 MPa and fracture toughness ≥ 5.8 MPa·m¹/², 3D Master ensures reliability for high-load restorations, minimizing fractures and rework.

Glaze n' Go!

Glaze n' Go!

No stain needed, accurate shading and Seamless 3D effect gurantees natural-looking restorations.

Consistent aesthetic results

Consistent aesthetic results

A flexible sintering range of 1520℃ to 1560℃ gives you the freedom to achieve stable and reliable outcomes every time.

Peace of Mind

Peace of Mind

Low deformation and high fracture toughness (≥ 5.8 MPa·m¹/²) ensure accurate, durable bridges—minimizing fractures and reducing case rework.

Efficient sintering

Efficient sintering

It achieves high-speed sintering with the BSM-FC30 and its specific sintering curve—enhancing efficiency and reducing delivery time.

Material Properties

Material Properties

  • Flexural strength (3 point)
    800-1200 MPa
  • Translucency
    43-51%
  • Vickers-hardness HV10
    1250-1350
  • Sintered Density
    > 6.02 g/cm³
  • Fracture toughness
    > 5.2 MPa.m 1/2
  • System
    98.5mm, 95mm (customized) etc.
  • Shade
    A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4, 0M1, 0M2, 0M3
  • Disc thickness (Ø 98.5 mm)
    12/14/16/18/20/22/25

Related documents

Contact us
×
Register for the Event
Fill in the form below to secure your spot!
I agree to the 《Privacy Policy》and to receive marketing communications.
Register Now
User Login
Forgot passwordDon't have an account?Register now
User registration
Forgot password
Confirm
Registration Agreement

dadasd